OrinBio@ PLA Resin HT series is divided into high heat resistant PLA, standard PLA and low heat resistant PLA, which are suitable for different polymer processes.
PLA has many applications in extrusion, injection molding, film drawing, spinning and other fields.
| Item | Unit | Test Method | HT101 | HT102 | HT103 | HT201 | HT202 | HT203 | HT301 | HT302 | HT303 |
| Moldinging Method | Modifiable,Extrusion molding,Blister molding,Thermoforming | Modifiable,Extrusion molding,Blister molding,Thermoforming | Modifiable,Extrusion molding,Blister molding,Thermoforming | Modifiable,Injection molding | Modifiable,Injection molding | Modifiable,Injection molding | FDM 3D print | Extrusion molding | FDM 3D print | ||
| Density | g/cm3 | GB/T1033.1-2008 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 |
| Melt Flow Rate | g/10min 190℃/2.16kg | GB/T3682.1-2018 | 2-9 | 2-9 | 2-9 | 10-25 | 10-25 | 10-25 | 2-6 | 2-6 | 2-6 |
| Melting temperature | ℃ | GB/T19466.3-2004 | ≥175 | 160-174 | <160 | ≥175 | 160-174 | <160 | 175 | 160-174 | <150 |
| Glass transition temperature | ℃ | GB/T19466.2-2004 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 |
| Tensile strength | MPa | GB/T1040.1-2018 | ≥55 | ≥50 | ≥50 | ≥45 | >45 | ≥45 | ≥55 | ≥50 | ≥45 |
| Elongation at Break | % | GB/T1040.1-2018 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 |
| Izod Notched Impact Strength | kJ/m2 4mm,23℃ | GB/T1043.1-2008 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 |
| Application | Heat-resistant straws, blister trays, food containers, cards, heat-resistant products, etc. | Blister trays, food containers, cards, etc. | Low heat-resistant blister products, transparent films, blister trays, food containers, cards, etc. | Disposable tableware, food containers, toys, other injection products, etc. | Disposable tableware, food containers, toys, other injection products, etc. | Disposable transparent tableware, food containers, toys, other injection products, etc. | 3D printing. | Straws. | 3D printing. | ||
| Feature | With high molecular weight and melt strength, high melting point and crystallinity, it can be used to produce heat-resistant polylactic acid extrusion, blister products, or heat-resistant products after proper modification. | With high molecular weight and melt strength, it can meet the corresponding process requirements. | With high molecular weight and melt strength, low crystallinity, can be used to produce low-resistance, high transparency polylactic acid film, blister products. | With good fluidity, high melting point and crystallinity, it can be used to produce heat-resistant polylactic acid injection products, or heat-resistant injection molding and blister products after proper modification. | With good fluidity, moderate melting point and crystallinity, it can be used to produce heat-resistant polylactic acid injection molding products. | With good fluidity, low melting point and slow crystallinity, it can be used to produce low-resistance, high transparency polylactic acid injection molding products. | With high crystallization rate and melt stability, it meets the requirements of FDM 3D printing molding process, and with appropriate heating process, it can produce heat-resistant 3D printing products | With appropriate crystallization rate and melt strength, which can meet the requirements of the molding process as a straw, and can also be blended with other types of biodegradable plastics to produce modified straws. | Amorphous polylactic acid resin, suitable for 3D printing molding process, with high bond strength between layers. |
· For availability and more model parameters, please contact account manager.
8 Product Application：
Disposable Tableware、Film Product、Packing Product、Textile Product、Electronics Product、Car Industry、3D Printing、Medical Filed
JJ 、BPI、OK Compost Home、Ok Compost Industrial
ISO9001、OHSAS18001、ISO45001、ISO17025、ISO14001
ORINKO since2008， listed in 2021， is a national high-tech enterprise which specialize in the research、 development、 production and sales of modified materials. It provides a full range of modified polyethylene, polyolefin, polyester, and polyamide products and also provide overall solutions of materials to customers.
the company is headquartered in Hefei, and currently has two production bases in Hefei and Chongqing, it builds a domestic first-class intelligent production plant for modified materials , and achieved an annual output and sales volume of over 1000,000 tons.
1.Are you a trading company or a manufacturer?
-We are a high-tech enterprise specializing in R&D, production and sales of polymer compounds, and dedicated to developing high performance Polymer Materials.Including BioPlastics, Polyolefins, Polystyrenes, Polyethylene, Engineering Plastics etc.
2.What's your biodegradeble resin range?
-We have a series of modified biodegradable materials.They are used in garbage bags, shopping bags, disposable tableware, 3D printing and electrical product casings.
3.I want some special purpose biodegradable raw materials,can you help me?
-Yes,that's our honor,we have a R&D team of more than 350 people, and more than 100 patents,created more than 300 kinds of polymer modified materials its products to our customers that perform in their own markets and meet product performance criteria at reasonable cost.
We can enhance the biodegradable resins of heat resistance, hardness, strength of finished products for you.
OrinBio@ PLA Resin HT series is divided into high heat resistant PLA, standard PLA and low heat resistant PLA, which are suitable for different polymer processes.
PLA has many applications in extrusion, injection molding, film drawing, spinning and other fields.
| Item | Unit | Test Method | HT101 | HT102 | HT103 | HT201 | HT202 | HT203 | HT301 | HT302 | HT303 |
| Moldinging Method | Modifiable,Extrusion molding,Blister molding,Thermoforming | Modifiable,Extrusion molding,Blister molding,Thermoforming | Modifiable,Extrusion molding,Blister molding,Thermoforming | Modifiable,Injection molding | Modifiable,Injection molding | Modifiable,Injection molding | FDM 3D print | Extrusion molding | FDM 3D print | ||
| Density | g/cm3 | GB/T1033.1-2008 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 |
| Melt Flow Rate | g/10min 190℃/2.16kg | GB/T3682.1-2018 | 2-9 | 2-9 | 2-9 | 10-25 | 10-25 | 10-25 | 2-6 | 2-6 | 2-6 |
| Melting temperature | ℃ | GB/T19466.3-2004 | ≥175 | 160-174 | <160 | ≥175 | 160-174 | <160 | 175 | 160-174 | <150 |
| Glass transition temperature | ℃ | GB/T19466.2-2004 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 | 58-62 |
| Tensile strength | MPa | GB/T1040.1-2018 | ≥55 | ≥50 | ≥50 | ≥45 | >45 | ≥45 | ≥55 | ≥50 | ≥45 |
| Elongation at Break | % | GB/T1040.1-2018 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 |
| Izod Notched Impact Strength | kJ/m2 4mm,23℃ | GB/T1043.1-2008 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 | <5 |
| Application | Heat-resistant straws, blister trays, food containers, cards, heat-resistant products, etc. | Blister trays, food containers, cards, etc. | Low heat-resistant blister products, transparent films, blister trays, food containers, cards, etc. | Disposable tableware, food containers, toys, other injection products, etc. | Disposable tableware, food containers, toys, other injection products, etc. | Disposable transparent tableware, food containers, toys, other injection products, etc. | 3D printing. | Straws. | 3D printing. | ||
| Feature | With high molecular weight and melt strength, high melting point and crystallinity, it can be used to produce heat-resistant polylactic acid extrusion, blister products, or heat-resistant products after proper modification. | With high molecular weight and melt strength, it can meet the corresponding process requirements. | With high molecular weight and melt strength, low crystallinity, can be used to produce low-resistance, high transparency polylactic acid film, blister products. | With good fluidity, high melting point and crystallinity, it can be used to produce heat-resistant polylactic acid injection products, or heat-resistant injection molding and blister products after proper modification. | With good fluidity, moderate melting point and crystallinity, it can be used to produce heat-resistant polylactic acid injection molding products. | With good fluidity, low melting point and slow crystallinity, it can be used to produce low-resistance, high transparency polylactic acid injection molding products. | With high crystallization rate and melt stability, it meets the requirements of FDM 3D printing molding process, and with appropriate heating process, it can produce heat-resistant 3D printing products | With appropriate crystallization rate and melt strength, which can meet the requirements of the molding process as a straw, and can also be blended with other types of biodegradable plastics to produce modified straws. | Amorphous polylactic acid resin, suitable for 3D printing molding process, with high bond strength between layers. |
· For availability and more model parameters, please contact account manager.
8 Product Application：
Disposable Tableware、Film Product、Packing Product、Textile Product、Electronics Product、Car Industry、3D Printing、Medical Filed
JJ 、BPI、OK Compost Home、Ok Compost Industrial
ISO9001、OHSAS18001、ISO45001、ISO17025、ISO14001
ORINKO since2008， listed in 2021， is a national high-tech enterprise which specialize in the research、 development、 production and sales of modified materials. It provides a full range of modified polyethylene, polyolefin, polyester, and polyamide products and also provide overall solutions of materials to customers.
the company is headquartered in Hefei, and currently has two production bases in Hefei and Chongqing, it builds a domestic first-class intelligent production plant for modified materials , and achieved an annual output and sales volume of over 1000,000 tons.
1.Are you a trading company or a manufacturer?
-We are a high-tech enterprise specializing in R&D, production and sales of polymer compounds, and dedicated to developing high performance Polymer Materials.Including BioPlastics, Polyolefins, Polystyrenes, Polyethylene, Engineering Plastics etc.
2.What's your biodegradeble resin range?
-We have a series of modified biodegradable materials.They are used in garbage bags, shopping bags, disposable tableware, 3D printing and electrical product casings.
3.I want some special purpose biodegradable raw materials,can you help me?
-Yes,that's our honor,we have a R&D team of more than 350 people, and more than 100 patents,created more than 300 kinds of polymer modified materials its products to our customers that perform in their own markets and meet product performance criteria at reasonable cost.
We can enhance the biodegradable resins of heat resistance, hardness, strength of finished products for you.