Typical Display | PLA Resin | Modified Biodegradable Material | ||||||||
HT102 | HT202 | HT503 | M1000 | M2000 | M5000-5C | H8000-1A | H8000-2D | H8000-3D | ||
Application process | Blow Molding | ● | ● | ● | ● | ● | ||||
Extrusion/Thermoforming | ● | ● | ● | |||||||
Injection Molding | ● | ● | ||||||||
Density | g/cm3 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.20-1.30 | 1.20-1.30 | 1.25-1.45 | 1.30-1.34 | 1.32-1.35 | |
Melt Flow Rate | （g/10min) 190℃ /2.16kg | 2-9 | 10-25 | 2-6 | 2-4 | 2-4 | 2-4 | 4-6 | 4-7 | |
Melting temperature | ℃ | 160-174 | 160-174 | <160 | / | / | / | / | / | |
Glass transition temperatur | ℃ | 58-62 | 58-62 | 58-62 | / | / | / | / | / | |
Tensile strength | MPa | ≥50 | ≥45 | ≥50 | ≥12 | ≥14 | ≥12 | ＞40 | ＞50 | |
Elongation at break | % | ＜5 | ＜5 | ＜5 | ≥350 | ≥300 | ≥250 | ＞5 | ＞5 | |
Typical Display | PLA Resin | Modified Biodegradable Material | ||||||||
HT102 | HT202 | HT503 | M1000 | M2000 | M5000-5C | H8000-1A | H8000-2D | H8000-3D | ||
Application process | Blow Molding | ● | ● | ● | ● | ● | ||||
Extrusion/Thermoforming | ● | ● | ● | |||||||
Injection Molding | ● | ● | ||||||||
Density | g/cm3 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.20-1.30 | 1.20-1.30 | 1.25-1.45 | 1.30-1.34 | 1.32-1.35 | |
Melt Flow Rate | （g/10min) 190℃ /2.16kg | 2-9 | 10-25 | 2-6 | 2-4 | 2-4 | 2-4 | 4-6 | 4-7 | |
Melting temperature | ℃ | 160-174 | 160-174 | <160 | / | / | / | / | / | |
Glass transition temperatur | ℃ | 58-62 | 58-62 | 58-62 | / | / | / | / | / | |
Tensile strength | MPa | ≥50 | ≥45 | ≥50 | ≥12 | ≥14 | ≥12 | ＞40 | ＞50 | |
Elongation at break | % | ＜5 | ＜5 | ＜5 | ≥350 | ≥300 | ≥250 | ＞5 | ＞5 | |