ORINKO Plastic Raw Material Nylon Pellets Pa6 Pa66 PA610 PA612 PA1012 resin for Automobile

ORINKO Plastic Raw Material Nylon Pellets Pa6 Pa66 PA610 PA612 PA1012 resin for Automobile

PA66 This resin offers a well-balanced combination of engineering properties characterized

Feature Description：

by high strength;

Good toughness; 

High impact; 

Good flow and surface lubricity;

Abrasion resistance; 

Resistant low temperature; 

Selfextinguishment.

PA612 has lower density，better transparence，lower water absorption，higher dimension stability，better chemical resistance，and higher impact resistance.

Feature Description：

Low water absorption

Good dimension stability

Good oil resistance, alkali resistance

High toughness, high strength

Low molding shrinkage

Excellent mouldability

PA610 Item	Test Standard	Unit	Typical Value
			Low viscosity	Medium viscosity	High viscosity
Viscosity number	GB/T 12006 ISO 307	cm3/g	110±20	145±15	180±20
Melting rang（Polarizing-microscope method）	GB/T 16582 ISO 3146	℃	222±5	222±5	222±5
Density	GB/T 1033 ISO 1183	kg/m3	1080±2	1080±2	1080±2
Tensile strength	GB/T 1040 ISO 572-1/-2	MPa	＞55	＞55	＞55
Tensile modulus	GB/T 1040 ISO 572-1/-2	MPa	＞2000	＞2000	＞2000
Tensile strain at break	GB/T 1040 ISO 572-1/-2	%	≥100	≥100	≥100
Charpy impact strength（+23℃）	GB/T 1043 ISO 179/1eU	kJ/m2	N	N	N
Charpy impact strength（-30℃）	GB/T 1043 ISO 179/1eU	kJ/m2	N	N	N
Charpy notched impact strength（+23℃）	GB/T 1043 ISO 179/1eA	kJ/m2	4	4	4
Charpy notched impact strength（-30℃）	GB/T 1043 ISO 179/1eA	kJ/m2	5	5	5